产品详情
规格
|
品牌 |
化学成分% |
|||||||
|
Si |
AI |
Ca |
Mn |
Cr |
P |
S |
C |
|
|
范围 |
≤ |
|||||||
|
FeSi75AI0.5-A |
74.0-80.0 |
0.5 |
1.0 |
0.4 |
0.3 |
0.035 |
0.020 |
0.1 |
|
FeSi75AI0.5-B |
72.0-80.0 |
0.5 |
1.0 |
0.5 |
0.5 |
0.040 |
0.020 |
0.2 |
|
FeSi75AI1.0-A |
74.0-80.0 |
1.0 |
1.0 |
0.4 |
0.3 |
0.035 |
0.020 |
0.1 |
|
FeSi75AI1.0-B |
72.0-80.0 |
1.0 |
1.0 |
0.5 |
0.5 |
0.040 |
0.020 |
0.2 |
|
FeSi75AI1.5-A |
74.0-80.0 |
1.5 |
1.0 |
0.4 |
0.3 |
0.035 |
0.020 |
0.1 |
|
FeSi75AI1.5-B |
72.0-80.0 |
1.5 |
1.0 |
0.5 |
0.5 |
0.040 |
0.020 |
0.2 |
|
FeSi75AI2.0-A |
74.0-80.0 |
2.0 |
1.0 |
0.4 |
0.3 |
0.035 |
0.020 |
0.1 |
|
FeSi75AI2.0-B |
74.0-80.0 |
2.0 |
1.0 |
0.4 |
0.3 |
0.040 |
0.020 |
0.1 |
|
FeSi75AI2.0-C |
72.0-80.0 |
2.0 |
|
0.5 |
0.5 |
0.040 |
0.020 |
0.2 |
|
FeSi75-A |
74.0-80.0 |
|
|
0.4 |
0.3 |
0.035 |
0.020 |
0.1 |
|
FeSi75-B |
74.0-80.0 |
|
|
0.4 |
0.3 |
0.040 |
0.020 |
0.1 |
|
FeSi75-C |
72.0-80.0 |
|
|
0.5 |
0.5 |
0.040 |
0.020 |
0.2 |
应用
1. 用于钢铁工业中的脱氧剂和合金剂。为了获得化学成分合格的钢并保证钢的质量，必须在炼钢阶段进行脱氧。硅和氧具有很强的化学亲和力，因此硅铁是炼钢中用于析出和扩散脱氧的强脱氧剂。. 向钢中加入一定量的硅可以显著提高钢的强度、硬度和弹性。因此，在冶炼结构钢（0.4%～1.75%Si）、工具钢（0.3%～1.8%Si）、弹簧钢（0.4%～2.8%Si）和变压器硅钢（2.81%～4.8%Si）时，硅铁也用作合金剂。同时，改善夹杂物的形状和减少钢水中气体元素的含量是提高钢材质量、降低成本和节约铁的有效新技术。它特别适用于连铸钢水的脱氧要求。实践证明，硅铁不仅满足炼钢的脱氧要求，而且具有脱硫性能，并具有比重较大、渗透力强的优点。
此外，在炼钢工业中，硅铁粉在高温下释放大量热量，常被用作钢锭帽的加热剂，以提高钢锭质量和回收率。
2. 它在铸铁工业中用作孕育剂和球化剂。铸铁是现代工业中重要的金属材料。它比钢便宜，易于熔化和冶炼，具有优良的铸造性能，抗冲击性能远优于钢。特别是球墨铸铁，其力学性能可与钢媲美或接近。向铸铁中加入一定量的硅铁可以防止铁中形成碳化物，并促进石墨的析出和球化。因此，在球墨铸铁生产中，硅铁是重要的孕育剂（有助于石墨析出）和球化剂。
3. 用于铁合金生产中的还原剂。硅和氧的化学亲和力不仅高，而且高硅硅铁的含碳量也很低。因此，高硅硅铁（或硅质合金）是铁合金工业中生产低碳铁合金常用的还原剂。
4. 75#硅铁常用于镁冶炼中Pidgeon法金属镁的高温冶炼过程。替代CaO,MgO中的镁，每生产一吨金属镁约消耗1.2吨硅铁。金属镁的生产起着重要作用。
5. 其他用途。磨细或雾化的硅铁粉可作为选矿工业中的悬浮相。它可用作焊条制造工业中的焊条涂层。高硅硅铁用于化工行业制造硅胶等产品。
在这些用途当中，炼钢、铸造和铁合金工业是硅铁的用户。它们一起消耗了大约90%的硅铁。在各种牌号的硅铁中，目前75%硅铁应用广泛。在炼钢工业中，每生产一吨钢消耗3-5公斤75%硅铁。